Composites were prepared using polyvinyl chloride (PVC) and different percentages of Fe2O3 nanoparticles. All composites were characterized by FT-IR spectroscopy. Then, the thermal properties of the composites prepared in 1% and 10% ratios were examined. It was observed that the initial decomposition temperature (Ti) values of PVC composites prepared with Fe2O3 nanoparticles addition were lower than pure PVC. Magnetic properties of composites were examined with a vibrating sample magnetometer (VSM). The saturation magnetization values of PVC composites prepared by using 1% and 10% Fe2O3 were 2.77 and 7.06 emu / g, respectively.
Polivinil klorür (PVC) ve farklı oranlarda Fe2O3 nanoparçacıkları kullanılarak kompozitler hazırlandı. Tüm kompozitler FT-IR spektroskopisi ile karakterize edildi. Ardından, %1 ve %10 oranlarında hazırlanan kompozitlerin termal özellikleri incelendi. Fe2O3 nanopartikül ilavesi ile hazırlanan PVC kompozitlerin başlangıç bozunma sıcaklığı (Ti) değerlerinin saf PVC'ye göre daha düşük olduğu görüldü. Titreşimli numune manyetometresi (VSM) ile kompozitlerin manyetik özellikleri incelendi. %1 ve %10 Fe2O3 kullanılarak hazırlanan PVC kompozitlerin doygunluk manyetizasyon değerleri sırasıyla 2,77 ve 7,06 emu/g bulundu.
Birincil Dil | İngilizce |
---|---|
Konular | Mühendislik |
Bölüm | Makaleler |
Yazarlar | |
Yayımlanma Tarihi | 30 Haziran 2022 |
Gönderilme Tarihi | 11 Eylül 2021 |
Kabul Tarihi | 22 Aralık 2021 |
Yayımlandığı Sayı | Yıl 2022 Cilt: 8 Sayı: 1 |